| Patent application number | Description | Published |
|---|
| 20080268152 | Composite sol, process for producing the same, and ink-jet recording medium - A composite sol containing colloidal composite particles having a particle diameter measured by dynamic light scattering method of 20 to 500 nm, composed of colloidal silica particles having a specific surface area diameter of 3 to 100 nm and aluminum phosphate bonding the colloidal silica particles or coating and bonding the colloidal silica particles; a process for producing the composite sol; a coating composition for ink receiving layer containing the composite sol; and an ink jet recording medium having an ink receiving layer containing the composite sol. | 10-30-2008 |
| 20080293831 | Method for producing zirconia sol - A production method of a zirconia sol includes; (A) mixing a dicarboxylic acid compound with a zirconium compound in an aqueous medium, in which a molar ratio of the dicarboxylic acid compound is more than 1 and less than or equal to 10 per mol of zirconium atom in the zirconium compound, and (B) adding 0.7-2.5 mol of a water-soluble organic base per mol of the dicarboxylic acid compound contained in a mixture obtained by the process (A) to the mixture and then treating hydrothermally the resultant mixture. | 11-27-2008 |
| 20090032994 | Method for Manufacturing Slurry and Mold for Precision Casting - A manufacturing method for a slurry for the production of a precision casting mold that includes a zirconia sol and a refractory powder, and a manufacturing method for a precision casting mold that uses the slurry is provided. The present invention relates to a manufacturing method for a slurry for the production of a precision casting mold for a metal that includes a step in which an alkaline zirconia sol (A1) and a refractory powder (D) are mixed, the alkaline zirconia sol (A1) being obtained by a manufacturing method that includes a step (i), in which a zirconium salt (B1) is heated at 60 to 110° C. in an aqueous medium that includes a carbonate of quaternary ammonium, and a step (ii), in which a hydrothermal treatment is carried out at 100 to 250° C. In addition, the present invention relates to a manufacturing method for a slurry for the production of a precision casting mold for a metal that includes a step in which an acidic zirconia sol (C3) and a refractory powder (D) are mixed, the acidic zirconia sol (C3) being obtained by a manufacturing method that includes a step (I), in which an alkaline zirconia sol (A3) and a zirconium salt (B3) are mixed, and a step II, in which the obtained liquid mixture is caused to react at 80 to 250° C. | 02-05-2009 |
| 20090036556 | Acidic Zirconia Sol and Production Method of the Same - There is provided an acidic zirconia sol having compatibility of particle properties and binding properties, and a production method of the same. | 02-05-2009 |
| 20090088313 | Production Method of Alkaline Zirconia Sol - [Problems to be Solved] To provide a production method of an alkaline zirconia having compatibility of particle properties and binding properties. | 04-02-2009 |
| 20090148380 | Method for Producing Metal Oxide Particle - There is provided a method for stably producing metal oxide solid solution particle at low temperature, wherein an alkaline zirconia sol is used as a raw material which is mixed with a metal compound, and then dried and fired. Specifically, there is disclosed a method for producing metal oxide particle (A3) such as zirconia particle in which metal oxides are solid-solubilized, comprising: a step (I) for obtaining metal oxide (A2) sol such as zirconia sol containing a precursor of a metal oxide by mixing an alkaline zirconia (A1) sol which is obtained by a method including a step (i) for heating a zirconium salt (B2) at 60-110° C. in an aqueous medium containing a carbonate of quaternary ammonium and a step (ii) for performing a hydrothermal treatment at 110-250° C., with a compound (B1) containing an element selected from a group consisting of the group II and group III elements of the periodic table; and a step (II) for drying the thus-obtained sol and then firing a resultant substance at a temperature of 500-1200° C. | 06-11-2009 |
| 20100120925 | ACIDIC ZIRCONIA SOL AND PRODUCTION METHOD OF THE SAME - There is provided an acidic zirconia sol having compatibility of particle properties and binding properties, and a production method of the same. The acidic zirconia sol includes zirconia particles (a) having a particle diameter ranging from 20 to 300 nm in a content of 90 to 50% by mass, based on the mass of all zirconia particles, and zirconia particles (b) having a particle diameter of less than 20 nm in a content of 10 to 50% by mass, based on the mass of all zirconia particles. | 05-13-2010 |
| 20110274767 | PRODUCTION METHOD OF TITANIUM OXIDE SOL - There is provided a method for efficiently producing an anatase-type titanium oxide sol in an extremely advantageous dispersion state. The method comprises mixing a titanium alkoxide, an organic acid, and a quaternary ammonium hydroxide with water in a molar ratio of the organic acid of 0.4 to 4.0 relative to 1 mol of a titanium atom of the titanium alkoxide and in a molar ratio of the quaternary ammonium hydroxide of 0.8 to 1.9 relative to 1 mol of the organic acid to prepare an aqueous mixed solution having a concentration in terms of TiO | 11-10-2011 |