Patent application number | Description | Published |
20080199346 | WELD METAL OF HIGH-STRENGTH CR-MO STEEL - A weld metal of a high-strength Cr—Mo steel formed by shielded metal arc welding contains: 0.04 to 0.10% by mass C, 0.15 to 0.5% by mass Si, 0.5 to 1.0% by mass Mn, 2.00 to 3.25% by mass Cr, 0.9 to 1.2% by mass Mo, 0.01 to 0.03% by mass Nb, 0.2 to 0.7% by mass V, 0.003% by mass or below and above 0% by mass B, 0.02 to 0.05% by mass O, and the balance of Fe and inevitable impurities. A residual extracted by electrolytic extraction from only an unaffected zone of the weld metal contains precipitated Cr in a Cr content below 0.3% by mass, and precipitated Nb in a Nb content of 0.005% by mass or above. | 08-21-2008 |
20120294752 | WELDING METAL HAVING EXCELLENT LOW-TEMPERATURE TOUGHNESS AND DROP-WEIGHT CHARACTERISTICS - Provided is a welding metal in which a predetermined chemical component composition is satisfied, the A value as specified by formula (1) is 3.8% to 9.0%, and the surface area percentage of carbide having a circle-equivalent diameter of 0.20 μm or greater in the welding metal is 4.0% or less. | 11-22-2012 |
20130028782 | WELDING METAL HAVING EXCELLENT LOW-TEMPERATURE TOUGHNESS AND DROP-WEIGHT CHARACTERISTICS - Provided is a welding metal in which the chemical component composition thereof is appropriately controlled; an A value that is specified by a predetermined relational expression satisfies the requirement of being 3.8% to 9.0%; an X value that is specified by a predetermined relational expression satisfies the requirement of being 0.5% or greater; the area percentage of carbide particles having a circle-equivalent diameter of 0.20 μm or greater in the welding metal is 4.0% or less; and the number of carbide particles having a circle-equivalent diameter of 1.0 μm or greater is 1000 particles/mm | 01-31-2013 |
20130270246 | WELDING SOLID WIRE AND WELD METAL - The objective of the present invention is to provide a similar-metal-composition welding solid wire, and weld metals therefor, with which both excellent bead shape and high ultralow-temperature toughness for the weld joints can be achieved when welding 9% Ni steels together by means of a high-efficiency MIG welding method. A fixed ratio of a REM and O are included in a similar-metal-composition welding solid wire of a 9% NI steel base material, and oxygen is supplied in a trace amount in a range that does not hinder the ultralow-temperature toughness of the weld joint ( | 10-17-2013 |